AlN ceramic was successfully wetted and then joined with nonactive Sn9Zn eutectic solder assisted by ultrasonication in air. The effect of ultrasonic time on the formation of joint was studied. Results indicated that the defect-free joint can be obtained at an ultrasonic time of 5 s. Two regions, namely, AlN/Sn (s,_s) and AlN/Zn (s,_s), were found in the bonding interface. Zn and O accumulated in the AlN/Sn (s,_s) interface. An amorphous and nanocrystalline layer of ZnO formed in the hard-wet AlN surface. And Zn (s,_s) directly bonded with AlN. The low temperature and fast bonding of the AlN was attributed to the high pressure and temperature caused by cavitation effect. The shear strength of the joint increased from 10.6 MPa to 30.7 MPa when the ultrasonic treatment time increased from 5 s to 150 s. With the prolongation of ultrasonic time, more AlN ceramic particles entered the solder and acted as the reinforcing phase.     

Thermal reliabilities of Sn-0.5Ag-0.7Cu-0.1Al2O3/Cu solder joint

The effects of trace addition of Al₂O₃ nanoparticles (NPs) on thermal reliabilities of Sn-0.5Ag-0.7Cu/Cu solder joints were investigated. Experimental results showed that trace addition of Al₂O₃ NPs could increase the isotheraml aging (IA) and thermal cyclic (TC) lifetimes of Sn-0.5Ag-0.7Cu/Cu joint from 662 to 787 h, and from 1597 to 1824 cycles, respectively. Also, trace addition of Al₂O₃ NPs could slow down the shear force reduction of solder joint during thermal services, which was attributed to the pinning effect of Al₂O₃ NPs on hindering the growth of grains and interfacial intermetallic compounds (IMCs). Theoretically, the growth coefficients of interfacial IMCs in IA process were calculated to be decreased from 1.61×10^-10 to 0.79×10^-10 cm²/h in IA process, and from 0.92×10^-10 to 0.53×10^-10 cm²/h in TC process. This indicated that trace addition of Al₂O₃ NPs can improve both IA and TC reliabilities of Sn-0.5Ag- 0.7Cu/Cu joint, and a little more obvious in IA reliability.     

A Modular Solder System with Hierarchical Morphology and Backward Compatibility

A modular solder system with hierarchical morphology and micro/nanofeatures in which solder nanoparticles are distributed on the surface of template micropowders is reported. A core–shell structure of subsidiary nanostructures, which improved the intended properties of the modular solder is also presented. In addition, polymer additives can be used not only as an adhesive (like epoxy resin) but also to impart other functions. By combining all of these, it is determined that the modular solder system is able to increase reflowability on a heat‐sensitive plastic substrate, oxidation resistance, and electrical conductivity. In this respect, the system could be readily modified by changing the structure and composition of each constituent and adopting backward compatibility with which the knowledge and information attained from a previously designed solder can offer feedback toward further improving the properties of a newly designed one. In practice, In–Sn–Bi nanoparticles engineered on the surface of Sn–Zn micropowders result in pronounced reflowing on a flexible Au‐coated polyethylene terephthalate (PET) substrate even at the low temperature of 110 °C. Depending on their respective concentrations, the incorporation of CuO@CeO₂ nanostructures and poly(3,4‐ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS) polymers increases oxidation resistance and electrical conductivity of the modular solder.     

Shear analysis of rice husk ash (RHA) reinforced tin-0.7-copper composite solders on electroless nickel/immersion silver (ENIAg) surfaces

In this study, the mechanical performance of the rice husk ash-reinforced tin-0.7 copper composite solder was investigated. 0.01 wt.%, 0.05 wt.% and 0.1 wt.% of rice husk ash (RHA) were added to the solder matrix to prepare the composite solders. In order, to replace the costly electroless nickel immersion gold surface finish on the copper substrate, the effect of electroless nickel immersion silver (ENIAg) as the surface finish was studied. The differential scanning calorimetry (DSC) analysis showed that the composite solder exhibited lower melting temperature relative to the plain solder owing to the inclusion of rice husk ash. Shear strength analysis was carried out to investigate the influence of rice husk ash and electroless nickel immersion silver surface finish on the shear strength of the developed composite solders. The results proved that the rice husk ash failed to enhance the shear strength of tin-0.7 copper lead-free solder with the plain solder exhibiting the highest shear strength.     

三河尖煤矿高应力区冲击矿压动态防治实践

介绍三河尖矿采用动态防治的方法，在具有冲击倾向的9202工作面高应力地区成功防治冲击矿压的技术实践。     

深井高应力难采煤层上行卸压开采的研究与实践

以新汶矿区为工程背景，深入研究了采动覆岩裂隙亚分带特征、覆岩运动与结构分带特征、上行卸压开采作用效应，建立了上行卸压开采可行程度的评价方法，论证了深井复合顶板煤层上行卸压开采的可行程度，通过应用实践根除了深井高应力难采煤层的多重障碍，为上行卸压开采的可行程度判别、区域划分、开采部署提供了决策依据。     

无铅BGA封装可靠性的力学试验与分析

着重研究了机械冲击和应力对无铅BGA封装焊点可靠性的影响,介绍了BGA封装的可靠性力学试验(跌落、弯曲试验)及其分析方法.通过对力学试验中失效焊点的分析以及借助ANSYS模拟工具,找出引起失效的根本原因,为开发性能更好、高可靠性的无铅材料、改进无铅工艺提供依据.     

BGA焊点的质量控制

BGA是现代组装技术的新概念,它的出现促进SMT(表面贴装技术)与SMD(表面贴装元器件)的发展和革新,并将成为高密度、高性能、多功能及高I/O数封装的最佳选择.本文结合实际工作中的一些体会和经验,就BGA焊点的接收标准、缺陷表现及可靠性等问题展开论述,特别对有争议的一种缺陷空洞进行较为详细透彻的分析,并提出一些改善BGA焊点质量的工艺改进的建议.     